Fast Formation Of Superhydrophobic Octadecylphosphonic Acid (ODPA) Coating For Self-cleaning And Oil/water Separation.
Chunai Dai, N. Liu, Yingze Cao, Y. Chen, F. Lu, L. Feng
Published 2014 · Materials Science, Medicine
Download PDFAnalyze on Scholarcy
A simple and fast method to prepare robust superhydrophobic octadecylphosphonic acid (ODPA) coating on oxidized copper mesh for self-cleaning and oil/water separation is reported here. The substrate of the copper mesh was first oxidized by simple immersion in an aqueous solution of 1.0 M NaOH and 0.05 M K2S2O8 at room temperature for 30 min, which was then covered with micro- and nanoscale Cu(OH)2 on the surface. Subsequently, the oxidized copper mesh was immersed in 2 × 10(-4) M octadecylphosphonic acid/tetrahydrofuran (ODPA/THF) solution, an ODPA coating formed on the oxidised copper mesh. The ODPA coating formation process takes place rapidly, almost in 1 second, which makes the as-prepared mesh exhibit superhydrophobicity with the water contact angle of approximately 158.9° and superoleophilicity with the oil contact angle of 0°. Moreover, the as-prepared mesh has self-cleaning effect and can be repeatedly used to efficiently separate a series of oil/water mixtures like gasoline/water and diesel/water. Interestingly, straightforward oxidation of a copper substrate produces a "water-removing" type oil/water separation mesh with underwater superoleophobicity, whereas ODPA coating on the oxidized copper mesh produces an "oil-removing" type oil/water separation mesh with superhydrophobicity and superoleophilicity. This interesting conversion results from a small amount of ODPA and takes place very rapidly.
This paper references
Delivering octadecylphosphonic acid self-assembled monolayers on a Si wafer and other oxide surfaces.
H. Nie (2006)
Robust self-assembled octadecylphosphonic acid monolayers on a mica substrate.
H. Nie (2005)
Bilayer and odd-numbered multilayers of octadecylphosphonic acid formed on a Si substrate studied by atomic force microscopy
H. Nie (2002)
Investigation of solid surfaces modified by Langmuir-Blodgett monolayers using sum-frequency vibrational spectroscopy and X-ray photoelectron spectroscopy.
T. Keszthelyi (2006)
Environmental nanotechnology: Nanomaterials clean up.
J. Lahann (2008)
Superwetting nanowire membranes for selective absorption.
Jikang Yuan (2008)
Mussel-inspired chemistry and Michael addition reaction for efficient oil/water separation.
Yingze Cao (2013)
Self-assembled monolayer growth of octadecylphosphonic acid on mica
J. Woodward (1996)
Lipophilic polyelectrolyte gels as super-absorbent polymers for nonpolar organic solvents.
Toshikazu Ono (2007)
New flexible aerogels and xerogels derived from methyltrimethoxysilane/dimethyldimethoxysilane co-precursors
Gen Hayase (2011)
Self-healing on OPA self-assembled monolayers
B. Neves (2001)
Self-assembled monolayers of n-alkanethiolates on copper are Barrier films that protect the metal against oxidation by air
P. E. Laibinis (1992)
A study of the inhibiton of copper corrosion by triethyl phosphate and triphenyl phosphate self-assembled monolayers
Wenjuan Guo (2006)
Superhydrophobic and superoleophilic properties of graphene-based sponges fabricated using a facile dip coating method
D. D. Nguyen (2012)
Thermal Stability Study of Self-Assembled Monolayers on Mica
B. Neves (2000)
Adsorption of toxic organic compounds from water with hydrophobic silica aerogels.
Suzana Štandeker (2007)
A Metallic Surface Corrosion Study in Aqueous NaCl Solutions Using Atomic Force Microscopy (AFM)
Andrew M. Skolnik (2000)
Use of Alkanethiol-Coated Electrodes To Study the Importance of Water Content on the Electrochemical Behavior of N-Ethyl-N‘-octadecyl Viologen on a Gold Electrode Surface
S. A. John (1999)
Fabrication of superhydrophobic TPU film for oil–water separation based on electrospinning route
L. Wang (2011)
Vertically-aligned carbon nano-tube membrane filters with superhydrophobicity and superoleophilicity
Cheesung Lee (2010)
Mechanisms and kinetics of self-assembled monolayer formation.
D. Schwartz (2001)
Recent developments in superhydrophobic surfaces with unique structural and functional properties
Y. Zhang (2012)
Performance and mechanism of a hydrophobic–oleophilic kapok filter for oil/water separation
X. Huang (2006)
Atomistic and energetic descriptions of self-assembled monolayers of differently endgroup-functionalized alkanethiols adsorbed on the gold substrate by using molecular simulations
G. Filippini (2013)
Self-assembled organic thin films on electroplated copper for prevention of corrosion
Y. S. Tan (2004)
Straightforward oxidation of a copper substrate produces an underwater superoleophobic mesh for oil/water separation.
N. Liu (2013)
Cover Picture: Champagne and Fireworks: Angewandte Chemie Celebrates Its Birthday (Angew. Chem. Int. Ed. 1/2013)
P. Gölitz (2013)
A hierarchical mesh film with superhydrophobic and superoleophilic properties for oil and water separation
J. Wu (2012)
Integrated oil separation and water purification by a double-layer TiO2-based mesh
Changrui Gao (2013)
Highly Oriented, Self-Assembled Alkanephosphate Monolayers on Tantalum(V) Oxide Surfaces
D. Brovelli (1999)
A super-hydrophobic and super-oleophilic coating mesh film for the separation of oil and water.
L. Feng (2004)
TiO2-based superhydrophobic–superhydrophilic patterns: Fabrication via an ink-jet technique and application in offset printing
S. Nishimoto (2009)
Self-Assembled Monolayers on Engineering Metals: Structure, Derivatization, and Utility
J. V. Alsten (1999)
3-Mercaptopropyltrimethoxysilane as a Cu corrosion inhibitor in KCl solution
R. Tremont (2000)
Bioinspired multifunctional foam with self-cleaning and oil/water separation
X. Zhang (2013)
Vapor phase self-assembly of fluorinated monolayers on silicon and germanium oxide
P. Hoffmann (1997)
Corrosion Inhibition by Thiol-Derived SAMs for Enhanced Wire Bonding on Cu Surfaces
C. Whelan (2004)
A novel superhydrophilic and underwater superoleophobic hydrogel-coated mesh for oil/water separation.
Z. Xue (2011)
Collagen based magnetic nanocomposites for oil removal applications
P. Thanikaivelan (2012)
SUBMONOLAYER ISLAND NUCLEATION AND GROWTH KINETICS DURING SELF-ASSEMBLED MONOLAYER FORMATION
Ivo Doudevski (1998)
Hydrolytic stability of organic monolayers supported on TiO2 and ZrO2.
S. Marcinko (2004)
Structure and order of phosphonic acid-based self-assembled monolayers on Si(100).
M. Dubey (2010)
Synthesis of stable super water- and oil-repellent polythiophene films.
Mael Nicolas (2006)
Low adhesion, non-wetting phosphonate self-assembled monolayer films formed on copper oxide surfaces.
E. Hoque (2009)
Superhydrophobic nanoporous polymers as efficient adsorbents for organic compounds
Y. Zhang (2009)
An introduction to ultrathin organic films from Langmuir-Blodgett to self-assembly: By Abraham Ulman, Academic Press, New York, 1991. xxiii + 442. $65.00
G. Gaines (1991)
Formation and Structure of Self-Assembled Monolayers.
A. Ulman (1996)
Chemical patterning and physical refinement of reactive superhydrophobic surfaces.
U. Manna (2012)
This paper is referenced by
Organic corrosion inhibitors : where are we now ? A review . Part IV . Passivation and the role of mono-and diphosphonates 1
A. Frumkin (2017)
Recent Development of Advanced Materials with Special Wettability for Selective Oil/Water Separation.
Qinglang Ma (2016)
Facile fabrication of robust superhydrophobic porous materials and their application in oil/water separation
Y. Hou (2015)
A robust 3D superhydrophobic sponge for in situ continuous oil removing
Huicai Wang (2018)
Preparation of Copper Alloys Based Low Surface Energy Composite Film and Its Corrosion Resistance
Gu Qiang (2018)
Micro/Nanoscale Structured Superhydrophilic and Underwater Superoleophobic Hybrid-Coated Mesh for High-Efficiency Oil/Water Separation
Teng Yuan (2020)
Fabrication of stable and durable superhydrophobic surface on copper substrates for oil-water separation and ice-over delay.
Jie Guo (2016)
A novel solution-controlled hydrogel coated mesh for oil/water separation based on monolayer electrostatic self-assembly
W. Zhang (2014)
A novel 3D porous modified material with cage-like structure: fabrication and its demulsification effect for efficient oil/water separation
Z. Wang (2017)
Recent Advances in the Fabrication of Superhydrophobic Surfaces
Q. Wen (2016)
Attachment of peri-implant pathogens to laser melted abutments and the development of a novel antimicrobial coating.
Clotilde Haury (2019)
Facile fabrication of superhydrophobic sand: Potential advantages for practical application in oil–water separation
Xuehu Men (2016)
Fabrication of Long-Term Underwater Superoleophobic Al Surfaces and Application on Underwater Lossless Manipulation of Non-Polar Organic Liquids
Jinlong Song (2016)
Water purification: oil–water separation by nanotechnology and environmental concerns
C. Lee (2017)
The nature of self-assembled octadecylphosphonic acid (ODPA) layers on copper substrates.
W. Zhao (2020)
One-step fabrication of robust fabrics with both-faced superhydrophobicity for the separation and capture of oil from water.
Jian Li (2015)
Advanced Sorbents for Oil-Spill Cleanup: Recent Advances and Future Perspectives.
Jin Ge (2016)
Polyphenylene sulfide microfiber membrane with superhydrophobicity and superoleophilicity for oil/water separation
H. Huang (2018)
Revestimentos a base de TEOS / ácido fosfônico como tratamento anticorrosivo para a liga AA 2024-T 3 TEOS / Phosphonic acid based coatings as anticorrosive treatment for AA 2024-T 3 alloy
S. W. Cendron (2016)
Facile fabrication of hydrogel coated membrane for controllable and selective oil-in-water emulsion separation.
Q. Zhang (2018)
Adsorption from Neutral Solutions of Sodium Alkyl Phosphonates on Zinc and Its Passivation
Y. Kuznetsov (2018)
Underwater superoleophobic meshes fabricated by poly(sulfobetaine)/polydopamine co-deposition
Peng-fei Ren (2015)
A self-cleaning polybenzoxazine/TiO2 surface with superhydrophobicity and superoleophilicity for oil/water separation.
W. Zhang (2015)
Bioinspired Lotus-like Self-Illuminous Coating.
Xiaodi Shi (2015)
Structure-Property Relationships of Nanosheeted 3D Hierarchical Roughness MgAl-Layered Double Hydroxide Branched to an Electrospun Porous Nanomembrane: A Superior Oil-Removing Nanofabric.
Z. Shami (2016)
Preparation of superhydrophobic films based on the diblock copolymer P(TFEMA-r-Sty)-b-PCEMA.
G. Zhang (2015)
Preparation and characterization of superhydrophobic composite coatings on a magnesium–lithium alloy
Z. Li (2016)
Fabrication of thin fluoropolymer adhered cotton fabric surface for efficiently microscopic to macroscopic level oil/water separation
Sukanta Pal (2019)
Biomimetics for Efficient Oil Water Separation: From Natural Oil Sorbents to Bioinspired Micro- and Nanostructured Polymeric Sorbents and Membranes
Claudia Zeiger (2018)
Fluorine-free superhydrophobic/hydrophobic polybenzoxazine/TiO2 films with excellent thermal stability and reversible wettability
W. Zhang (2015)
Versatile fabrication of magnetic carbon fiber aerogel applied for bidirectional oil–water separation
Y. Li (2015)
pH-Induced Switchable Superwettability of Efficient Antibacterial Fabrics for Durable Selective Oil/Water Separation.
Y. Fu (2017)See more