Preparation Of Hierarchic Porous Films Of α‐MnO2 Nanoparticles By Using The Breath Figure Technique And Application For Hybrid Capacitor Electrodes
Nobuhiro Shimamura, Ryuji Kanda, Yuma Matsukubo, Yutaro Hirai, H. Abe, Y. Hirai, T. Yoshida, H. Yabu, A. Masuhara
Published 2019 ·
Save to my Library
Download PDFAnalyze on Scholarcy
The honeycomb-structured film has advantages such as high wettability and high surface area. This structure and properties are suitable for the capacitor electrode. In this study, the electrode structure is controlled by the synthesis of MnO2 nanoparticles using the breath figure method. The electrode performance was calculated by electrochemical measurements. As a result, the capacitance value was 100.5 F/g at 1 mV s−1, which was improved 2.7 times as compared with that without structure control.
This paper references
Principles and applications of electrochemical capacitors. Electrochim
R. Kötz (2000)
Single-Step Fabrication of Transparent Superhydrophobic Porous Polymer Films
H. Yabu (2005)
Electrochemical supercapacitor studies of porous MnO2 nanoparticles in neutral electrolytes
S. R. Srither (2016)
Design of novel biointerfaces (II). Fabrication of self-organized porous polymer film with highly uniform pores.
M. Tanaka (2004)
Single-molecule mechanics of mussel adhesion
H. Lee (2006)
Ultrafast Charging-Discharging Capacitive Property of RuO2 Nanoparticles on Carbon Nanotubes Using Nitrogen Incorporation
W. Fang (2008)
Flexible Transparent Supercapacitors Based on Hierarchical Nanocomposite Films.
Fanhong Chen (2017)
Underwater Bonding with Charged Polymer Mimics of Marine Mussel Adhesive Proteins
J. White (2011)
Fabrication of selforganized porous polymer film with highly uniform pores
M Tanaka (2004)
Catalytic oxidation of formaldehyde over manganese oxides with different crystal structures
J. Zhang (2015)
microparticles composed of mesoporous manganese dioxide and fullerene C60
Y. Dou (2015)
Electrical conductivity and supercapacitor properties of polyaniline/chitosan/nickel oxide honeycomb nanocomposite
Mini Vellakkat (2017)
Mussel-inspired load bearing metal-polymer glues.
A. Stepuk (2012)
Breath Figure Method for Construction of Honeycomb Films
Y. Dou (2015)
Dispersion of Al2O3 nanoparticles stabilized with mussel-inspired amphiphilic copolymers in organic solvents and formation of hierarchical porous films by the breath figure technique.
Y. Saito (2013)
Synthesis of Nanostructured Mesoporous Manganese Oxides with Three-Dimensional Frameworks and Their Application in Supercapacitors
Yu-Ting Wang (2011)
Effect of Crystallographic Structure of MnO2 on Its Electrochemical Capacitance Properties
S. Devaraj (2008)
A versatile macro-initiator with dual functional anchoring groups for surface-initiated atom transfer radical polymerization on various substrates
Qiangbing Wei (2012)
Principles and applications of electrochemical capacitors
R. Kötz (2000)
Carbon properties and their role in supercapacitors
A. Pandolfo (2006)
Prevention of postoperative adhesions by a novel honeycomb-patterned poly(lactide) film in a rat experimental model.
Yukako Fukuhira (2008)
Materials for electrochemical capacitors.
P. Simon (2008)
Fabrication of hybridized microparticles composed of mesoporous manganese dioxide and fullerene C 60 nanocrystals
Y. Matsukubo (2018)
Electrochemical Capacitors for Energy Management
J. Miller (2008)
A review of electrode materials for electrochemical supercapacitors.
G. Wang (2012)
A review on electrochemical doublelayer capacitors
P. Sharma (2010)
Synthesis and characterization of sol - processed α - MnO 2 nanostructures
D. Ramarajan (2012)
A reversible wet/dry adhesive inspired by mussels and geckos
H. Lee (2007)
How to Achieve Maximum Utilization of Hydrous Ruthenium Oxide for Supercapacitors
C. Hu (2004)
Effect of alkaline and alkaline–earth cations on the supercapacitor performance of MnO2 with various crystallographic structures
Chenchen Ji (2013)
Charge Storage Mechanism of MnO2 Electrode Used in Aqueous Electrochemical Capacitor
M. Toupin (2004)
Direct Observation of Dye-Containing Amphiphilic Copolymer in the Honeycomb-Patterned Film
Miki Kojima (2008)
Breath Figures of Nanoscale Bricks: A Universal Method for Creating Hierarchic Porous Materials from Inorganic Nanoparticles Stabilized with Mussel-Inspired Copolymers.
Y. Saito (2014)
Superior capacitive property of RuO2 nanoparticles on carbon nanotubes incorporated with nitrogen
W. Fang (2007)
Fabrication of mussel-inspired highly adhesive honeycomb films containing catechol groups and their applications for substrate-independent porous templates.
Y. Saito (2013)